| Abstract [eng] |
The aqueous sol-gel synthesis technique for the preparation of (Pb,Sr)Sr2(Y,Ca)Cu2O7±x (Pb–1212) and (Pb2,Cu)Sr2(Y,Ca)Cu2O8±x (Pb–3212) superconductors using two different complexing agents, namely 1,2-ethanediol and tartaric acid was studied. The phase transformations, composition and micro-structural features in the polycrystalline samples were studied by powder X-ray diffraction analysis (XRD), infrared spectroscopy (FTIR) and scanning electron microscopy (SEM). XRD analysis of the ceramic samples obtained by calcination of Pb-Sr-Y-Ca-Cu-O acetate-glycolate precursor gels in air, for 10 hours at 800°C and at 825°C, showed the presence of homogeneous Pb–1212 and Pb–3212 crystallites as major phases. The XRD patterns of the ceramics obtained from Pb-Sr-Y-Ca-Cu-O acetate-tartrate precursor gels, however, showed multiphasic character. The critical temperature of superconductivity (TC (onset)) observed by resistivity measurements were found to be 91 K and 75 K for Pb–1212 and Pb–3212 samples, respectively. |